Stainless Steel Plate
Sandmeyer Steel Company stocks Alloy 309/309S heat resistant stainless steel plate in thicknesses from 3/16" through 3".
Available thicknesses for Alloy 309/309S:
3/16" | 1/4" | 5/16" | 3/8" | 1/2" | 5/8" | 3/4" | 1" |
---|---|---|---|---|---|---|---|
4.8mm | 6.3mm | 7.9mm | 9.5mm | 12.7mm | 15.9mm | 19mm | 25.4mm |
1 1/4" | 1 1/2" | 1 5/8" | 1 3/4" | 2" | 2 1/2" | 3" | |
31.8mm | 38.1mm | 41.3mm | 44.5mm | 50.8mm | 63.5mm | 76.2mm |
Alloy 309/309S (UNS S30900/S30908) austenitic stainless steel is typically used for elevated temperature applications. Its high chromium and nickel content provides comparable corrosion resistance, superior resistance to oxidation, and the retention of a larger fraction of room temperature strength than the common austenitic Alloy 304.
Specification Sheet Overview
for Alloy 309/309S/309H (UNS S30900, S30908, S30909)
W. Nr. 1.4833:
![Stainless Steel Plate](/images/insideimage.jpg)
General Properties
Alloy 309 (UNS S30900) is an austenitic stainless steel developed for use in high temperature corrosion resistance applications. The alloy resists oxidation up to 1900∼F (1038∼C) under non-cyclic conditions. Frequent thermal cycling reduces oxidation resistance to approximately 1850∼F (1010∼C).
Because of its high chromium and low nickel content, Alloy 309 can be utilized in sulfur containing atmospheres up to 1832∼F (1000∼C). The alloy is not recommended for use in highly carburizing atmospheres since it exhibits only moderate resistance to carbon absorption. Alloy 309 can be utilized in slightly oxidizing, nitriding, cementing and thermal cycling applications, albeit, the maximum service temperature must be reduced.
When heated between 1202 每 1742∼F (650 每 950∼C) the alloy is subject to sigma phase precipitation. A solution annealing treatment at 2012 每 2102∼F (1100 每 1150∼C) will restore a degree of toughness.
309S (UNS S30908) is the low carbon version of the alloy. It is utilized for ease of fabrication. 309H (UNS S30909) is a high carbon modification developed for enhanced creep resistance. It most instances the grain size and carbon content of the plate can meet both the 309S and 309H requirements.
Alloy 309 can be easily welded and processed by standard shop fabrication practices.
Applications
- Furnaces 〞 burners, doors, fans, piping and recuperators
- Fluidized Bed Furnaces 〞 grids, piping, wind boxes
- Paper Mill Equipment
- Petroleum Refining 〞 catalytic recovery systems, recuperators
- Power Generation 〞 pulverized coal burners, tube hangers
- Thermal Processing 〞 annealing covers and boxes, burners grids, doors, fans, lead pans and neutral salt pots, muffles and retorts, recuperators, walking beams
- Waste Treatment 〞 incinerators, rotary kilns and calciners
Standards
ASTM........A 240
ASME........SA 240
AMS..........5523
Corrosion Resistance
Wet Corrosion
Alloy 309 is not designed for service in wet corrosive environments. The high carbon content, which is present to enhance creep properties, has a detrimental effect on aqueous corrosion resistance. The alloy is prone to intergranular corrosion after long term exposure at high temperatures. However, due to its high chromium content (23%), Alloy 309 is more corrosion resistant than most heat resistant alloys.
High Temperature Corrosion
Alloy 309 resists high temperature corrosion in most in-service conditions. Operating temperatures are as follows:
Oxidizing conditions (max. sulfur content 每 2 g/m3)
1922∼F (1050∼C) continuous service
2012∼F (1100∼C) peak temperature
Oxidizing conditions (max. sulfur greater than 2 g/m3)
1742∼F (950∼C) maximum temperature
Low oxygen atmosphere (max. sulfur content 每 2 g/m3)
1832∼F (1000∼C) maximum temperature
Nitriding or carburizing atmospheres
1562 每1742∼F (850 每 950∼C) maximum
The alloy does not perform as well as Alloy 600 (UNS N06600) or Alloy 800 (UNS N08800) in reducing, nitriding or carburizing atmospheres, but it does outperform most heat resistant stainless steels in these conditions.
Creep Properties
Typical Creep Properties
Temperature | Creep Strain (MPa) | Creep Rapture (MPa) | |||||
---|---|---|---|---|---|---|---|
°C | °F | 1000 H | 10000 H | 100000 H | 1000 H | 10000 H | 100000 H |
600 | 1112 | 120 | 80 | 40 | 190 | 120 | 65 |
700 | 1292 | 50 | 25 | 20 | 75 | 36 | 16 |
800 | 1472 | 20 | 10 | 8 | 35 | 18 | 7.5 |
900 | 1652 | 8 | 4 | 3 | 15 | 8.5 | 3 |
1000 | 1832 | 4 | 2.5 | 1.5 | 8 | 4 | 1.5 |
Chemical Analysis
Weight % (all values are maximum unless a range is otherwise indicated)
Element | 309 | 309S | 309H |
---|---|---|---|
Chromium | 22.0 min.-24.0 max. | 22.0 min.-24.0 max. | 22.0 min.-24.0 max. |
Nickel | 12.0 min.-15.0 max. | 12.0 min.-15.0 max. | 12.0 min.-15.0 max. |
Carbon | 0.20 | 0.08 | 0.04 min.-0.10 max. |
Manganese | 2.00 | 2.00 | 2.00 |
Phosphorus | 0.045 | 0.045 | 0.045 |
Sulfer | 0.030 | 0.030 | 0.030 |
Silicon | 0.75 | 0.75 | 0.75 |
Iron | Balance | Balance | Balance |
Physical Properties
Density
0.285 lbs/in37.89 g/cm3
Specific Heat
0.12 BTU/lb-∼F (32 每 212∼F)502 J/kg-∼K (0 每 100∼C)
Modulus of Elasticity
28.5 x 106 psi193 GPa
Thermal Conductivity 212∼F (100∼C)
9.0 BTU/hr/ft2/款喧/∼幛15.6 W/m-∼K
Melting Range
2500 每 2590∼F1480 每 1530∼C
Electrical Resistivity
30.7 Microhm-in at 68∼C78 Microhm-cm at 20∼C
Mechanical Properties
Typical Values at 68∼F (20∼C)
Yield Strength 0.2% Offset |
Ultimate Tensile Strength |
Elongation in 2 in. |
Hardness | ||
---|---|---|---|---|---|
psi (min.) | (MPa) | psi (min.) | (MPa) | % (min.) | (max.) |
45,000 | 310 | 85,000 | 586 | 50 | 202 (HBN) |
Fabrication Data
Alloy 309 can be easily welded and processed by standard shop fabrication practices.
Hot Forming
Heat uniformly at 1742 每 2192∼F (950 每 1200∼C). After hot forming a final anneal at 1832 每 2101∼F (1000 每 1150∼C) followed by rapid quenching is recommended.
Cold Forming
The alloy is quite ductile and forms in a manner very similar to 316. Cold forming of pieces with long-term exposure to high temperatures is not recommended since the alloy is subject to carbide precipitation and sigma phase precipitants.
Welding
Alloy 309 can be readily welded by most standard processes including TIG, PLASMA, MIG, SMAW, SAW and FCAW.
NOTE: The information and data in this product data sheet are accurate to the best of our knowledge and belief, but are intended for informational purposes only, and may be revised at any time without notice. Applications suggested for the materials are described only to help readers make their own evaluations and decisions, and are neither guarantees nor to be construed as express or implied warranties of suitability for these or other applications. Stainless Steel, Nickel Alloy and Titanium products are classified as sheet if the thickness of the metals is less than 3/16§ (4.7mm). If the thickness of the metal is 3/16§ (4.7mm) or more, then it is considered a plate.